Ushbu maqolada texnik uglerodning sanoat va energetika sohalarida qo‘llanilish xususiyatlari hamda uning strukturaviy va sirt koʻrsatkichlarini amaliy ahamiyati o‘rganildi. TU-5 markali texnik uglerod namunasi ASTM D1510, D1506 va D1509 standartlari asosida tahlil qilinib, uning yodni yutish qobiliyati (85.3 g/kg), kul miqdori (0.4 %) va massa yo‘qotilishi (0.33 %) aniqlangan. Olingan natijalar texnik uglerodning yuqori dispersligi, rivojlangan sirt maydoni va past uchuvchan komponentlar miqdoriga ega ekanligini ko‘rsatdi. Tadqiqot natijalari ushbu materialning rezina kompozitsiyalarida samarali mustahkamlovchi va texnologik jihatdan barqaror komponent sifatida qo‘llanishini ilmiy jihatdan asoslaydi.References
1. Conway B. E. Technology Development //Electrochemical Supercapacitors: Scientific Fundamentals and Technological Applications. Boston, MA: Springer US, 1999. С. 609-674.
2. Simon P., Gogotsi Y. Perspectives for electrochemical capacitors and related devices //Nature materials. 2020. Т. 19. №. 11. С. 1151-1163.
3. Hu S. et al. Recent Developments at the Interface of Carbon Fiber‐Reinforced Polymer Composites Theory, Modification and Interfacial Properties //Polymer Composites. 2026. Т. 47. №. 3. С. 1995-2023.
4. Robertson C. G., Hardman N. J. Nature of carbon black reinforcement of rubber: Perspective on the original polymer nanocomposite //Polymers. 2021. Т. 13. №. 4. С. 538.
5. Song Y., Huang D. Linear rheology of natural rubber compounds filled with silica, short nylon fiber or both //Polymer. 2018.Т. 134. С. 71-74.
6. Nchekwube F. N. Graphitization of recovered carbon black and N660 carbon black via spark plasma sintering: a comparative analysis: дис. University of British Columbia, 2025.
7. Barrera C. S., Cornish K. High performance waste-derived filler/carbon black reinforced guayule natural rubber composites //Industrial Crops and Products. 2016. Т. 86. С.
8. Speranza G. The role of functionalization in the applications of carbon materials: an overview //C. 2019. Т. 5. №. 4. С. 84.
9. Wang J. et al. Graphene-based hybrid fillers for rubber composites //Molecules. 2024. Т. 29. №. 5. С. 1009.
This work is licensed under a Creative Commons Attribution 4.0 International License.
Copyright (c) 2026 Tojimurodovich Ortiqov Nosir, Ubaydulla o'g'li Karimov Mas'ud, Turapovich Djalilov Abdulaxat (Author)